小端面側内径と内径のコッターのあたりの強い部分から破断したものと思われ

小端面側内径と内径のコッターのあたりの強い部分から破断したものと思われ、
疲労進展領域が確認されないため、衝撃的に負荷が増大したことによる破損であると考えられる。
分析より材質はSCr415H材である可能性が高く、また、起点付近に異物等は検出されなかった。

ผลลัพธ์ (อังกฤษ) 2:

Small end face side inner diameter and the inner diameter of around the Cotter of the strength we part from the break to those you think we ,
fatigue growth area is confirmed because they are not , shocking the load is increased and due to the fact that was damaged and is considered Erareru .
Analysis from the material is SCr415H material is likely that higher rather , also , near the origin of the foreign substance is detected was not .

ผลลัพธ์ (อังกฤษ) 3:

On the side of the small end face is said to have been broken pieces from around the inner diameter of the inner diameter of the joint development area was confirmed at the fatigue is not considered shocking failure is due to the fact that the load is increased. By the analysis of the material is high, and the possibility of SCr 415 H material near the starting point is detected by the foreign matter or the like. At